LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. LicenseException: Current version 5.2.375.133 is newer than required version 4.9999. Spring - Fagersta Stainless
Fagersta Stainless

Spring

  Nominal composition (* max value)
PDF Fagersta grades EN AISI/AWS Type DIN W-Nr. C Si Mn Cr Ni Mo Other
  Austenitic CWH **
R300.16 1.4310 302 1.4310 .07 .45 1.25 17.2 8.2 .50* N .040 135
R300.33 1.4310 1.4310 .09 .50 1.25 17.0 7.3 .60* N .070 154
R300.35 1.4310 302 1.4310 .08 .90 1.30 17.2 8.1 .60* Cu .50, N .045 139
R320.14 1.4301 302 1.4301 .05 .40 .75 17.8 8.6 .60* N .035 120
R320.15 302/304 1.4301 .06 .35 1.25 18.3 9.0 .60* N .060* 117
R320.17 1.4310 302/304 1.4310 .07 .45 1.25 18.3 8.1 .60* N .040 130
R359.12 1.4541 321 1.4541 .05 .60 1.70 17.3 9.2 .60* N .04, Ti .30  
R420.18 1.4401 316 1.4401 .05 .35 1.55 16.8 10.7 2.1 N .060* 102
R429.10 1.4571 1.4571 .06 .55 1.55 17.2 11.2 2.1 N .020* Ti .35  
R520.12 201 .09 .45 5.9 17.0 5.3 .60* N .070  
  Precip.hardening  
R560.20 (17-7 Ph) 1.4568 631 1.4568 .080 .40 .70 16.5 7.6 .50* Al 1.00  
  Duplex PRE
R617.10* 1.4162 .030 .70 5.0 21.5 1.5 .30 N .22 28
R630.21* 1.4362 .015 .45 .95 22.5 4.7 .54* Cu .54* N .110 26
R647.21* 1.4462 1.4462 .020 .55 .87 22.1 5.5 3.2 N .18 36

*) R617.10: Outokumpu LDX 2101
*) R630.21: SAF 2304
*) R647.21: SAF 2205

**) CWH: FSABs Cold Work Hardening-factor is a number calculated from a data-matrix of C, Cr and Ni contents, which increases with increasing work hardeening rate and can range between 80 to 160 depending on austenitic steel grade.

***) PRE: Pitting resistance equivalent.
         PRE: Cr + 3.1 x Mo + 25 x N